Aluminium profiles 0603 0601 Industrial aluminum profile Wood Grain Series-02

The imitated surface is unique,realistic,natural and splendid.

The imitated surface is unique,realistic,natural and splendid.It resiststs the aging,erosion and maintenance free,Therefore it grows up rapidly in the fields of architectural decoration,fitment,furniture.electron and home appliance,and it becomes one of the substitutes of the high class decoration aluminium profile.Decorating with aluminium instead of wood can reduce wood usages and protect ecological balance effectively.

Product Name	Powder Coated Aluminum Profile
Material	6060 6061 6063 7005,T5 T6
Surface Treatment	1.Surface treatment:Mill finish,silver anodize, matt anodize,blasting anodize,colored anodize,powder coating,electrophorsis,wooden shift
Color	All RAL color available
Model	We have over 30,000 kinds of products, we also welcome OEM product
Our Advantage	1)      Manufacture with lower price and high quality
	2)      Professional engineer with more than ten years designing experience
	3)      Strict QC to guarantee the high quality
Main products:	aluminium profile for windows and doors,curtain wall,extrusion profile,aluminium tube,pipe,panel,furniture profiles and produce as your design.
Primary Technical Data of  Aluminum Profile
Chemical composition
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Impurity	Al
6063	0.2-0.6	0.35	0.1	0.1	0.45-0.90	0.1	0.1	0.1	0.15	Rest
6061	0.4-0.8	0.7	0.15-0.40	0.15	0.8-1.2	0.04-0.35	0.25	0.15	0.15	Rest
6005	0.6-0.9	0.35	<0.1	<0.1	0.40-0.6	<0.1	<0.1	<0.1	<0.15	Rest
Mechanical property
Alloy	Condition		Tensile strength		Yield strength		Elongation		Vickers hardness
6061	T6		>265Mpa		>245Mpa		>8%
6063	T5		>160Mpa		>110Mpa		>8%		HV>58 HW>8
	T6		>205Mpa		>180Mpa		>8%
Colored anodized profile
Grade	Thickness of film				Hole scaling quality of oxide layer
	Average thickness		Local thickness		P. Cr acid-erosion weight less method
AA10	>10um		>8mm		<30 mg/d m2
AA15	>15um		>12um
Electrophoretic coating profiles
Grade	Anodic oxide film		Thickness of paint film		Thickness of complex film		Film hardness
	Average thickness	Local thickness
A	>10um	>8um	>12um		>21um		>3um
B	>10um	>8um	>7um		>17um		>3um
Powder coating & wooden-grained profile
Coating thickness	Coating impress rigidity		Adhesive force of coating layer
40-120um	Indentation hardness>80		0 grade
Thermal-break profile
type	Characteristic value of longitudinal shear strength Tc			Characteristic value of transverse strength Qc
Inserting	>24N/mm			>24N/mm
Pouring	>24N/mm			>24N/mm